Process for production of synthesis gas by oxidative conversion of methane or natural gas using composite catalysts

ABSTRACT

An improved process for the production of synthesis gas (or carbon monoxide and hydrogen) by oxidative conversion of natural gas or methane, which comprises passing continuously a gaseous reactant mixture comprising methane (or natural gas) and oxygen (or air) with or without water vapors over reduced or unreduced composite catalyst, containing non-transition and/or transition metal oxides, represented by the formula T m .sup.. N n .sup.. R.sup.. O p , wherein T is selected from Ni, CO, Ir or the like or a mixture thereof, m is T/R mole ratio, N is a transition or non-transition element selected from Ti, Zr, Hf, Zn, Mg, Ca or the like or a mixture thereof, n represents the N/R mole ratio, R is a rare earth element selected from La, Ce, Pr, Ho, Yb or the like, or a mixture thereof, O is oxygen and p is the number of oxygen atoms required to fulfill the valence requirement of the elements in the composite catalyst. Synthesis gas can be produced in high yields and with very high production rate by oxidative conversion of methane or natural gas to CO and H 2  or synthesis gas, using the composite catalyst containing non-transition and/or transition metal oxides.

This is a divisional of copending application(s) Ser. No. 07/930,007 filed on Aug. 14, 1992.

This invention relates to an improved process for the production of synthesis gas (or CO and H₂) by oxidative conversion of natural gas (or methane) using composite catalysts containing non-transition and/or transition metal oxides. The process of this invention is useful for the production of synthesis gas, or CO and H₂ from natural gas or methane. The process of the present invention could be used by the producers of synthesis gas, or CO and H₂ as well as by users of synthesis gas, or CO and H₂. For example, for those processes that produce methanol and methanol based products, Fischer-Tropsch synthesis products such as liquid hydrocarbons, olefins, alcohols and aldehydes, oxo-synthesis products, ammonia and ammonia based fertilizers and chemicals, town gas and reduction gas used for the production of sponge iron, etc.

BACKGROUND OF THE INVENTION

The conversion of methane or natural gas to carbon monoxide (CO) and hydrogen (H₂) or synthesis gas by catalytic steam reforming, autothermal catalytic reforming and non-catalytic partial oxidation, is known in the prior art.

The catalytic steam reforming of natural gas or methane to synthesis gas, or hydrogen and carbon monoxide is a well established technology practiced for commercial production of hydrogen, carbon monoxide and syngas (i.e. mixture of hydrogen and carbon monoxide). In this process, hydrocarbon feeds are converted to a mixture of H₂, CO and CO₂ by reacting hydrocarbons with steam over a catalyst (NiO supported on calcium aluminate, alumina, spinel type magnesium aluminum oxide or calcium aluminate titanate) at elevated temperature (850°-1000° C.) and pressure (10-40 atm) and at a steam/carbon mole ratio of 2-5 and gas hourly space velocity (based on wet feed) of about 5000-8000 per hour. This process involves the following reactions:

    CH.sub.4 +H.sub.2 O⃡CO+3H.sub.2

or

    C.sub.n H.sub.m +nH.sub.2 O⃡nCO+[n+(m/2)] H.sub.2

and

    CO+H.sub.2 O⃡CO.sub.2 +H.sub.2 (shift reaction)

The conversion is highly endothermic and is carried out in a number of parallel tubes packed with catalyst and externally heated by flue gas of temperature of 980°-1040° C. (Kirk and Othmer, Encyclopedea of Chemical Technology, 3rd Edn., 1990 vol. 12 p. 951; Ullamann's Encyclopedea of Industrial Chemistry, 5th Edn., 1989, vol. A-12 p. 186). The main drawbacks of this process are as follows. It is highly endothermic and operated at high temperature. Hence, it is highly energy intensive. Further, the shift reaction occurring in the process leads to formation of CO₂ and H₂ from CO and water, thus increasing H₂ /CO ratio. Since a lower H₂ /CO ratio than that obtained by the steam reforming is required for certain applications of synthesis gas, secondary reformer using CO₂ or O₂ oxidants are frequently required to reduce the hydrogen content of synthesis gas produced by the steam reforming. Also, the supported nickel catalyst used in the steam reforming is poisoned by sulfur containing compounds present in very low concentrations in the feed hydrocarbons. Further, there is a carbon deposition on the catalyst during the steam reforming.

Autothermal catalytic reforming of methane or natural gas with air or oxygen to H₂, CO and CO₂ is also an established technology. In this process, a feed gas mixture containing hydrocarbon, steam and oxygen (or air) is passed through a burner and then the combustion gases are passed over a catalyst (nickel supported on alumina) in a fixed bed reactor at 850°-1000° C. and 20-40 atm. (Ullamann's Encyclopedea of Industrial Chemistry 5th Edn., 1989, vol. A-12, p. 202). This process has the following drawbacks. There are large temperature and space velocity variations during start-up and shut down which leads to abrasion and catalyst disintegration, requiring frequent refilling and removal of the catalyst. This process operates at high temperature and pressure and there is a formation of carbon (or carbon deposition) in the reactor.

Non-catalytic partial oxidation of hydrocarbons to H₂, CO and CO₂ is an established technology used mostly for producing hydrogen from heavy fuel oils, primarily in locations where natural gas or lighter hydrocarbons, including naphtha, were unavailable or were uneconomical as compared with fuel oil or crude oil. This process is carried out by injecting preheated hydrocarbon, oxygen and steam through a specially designed burner into a closed combustion chamber, where partial oxidation of the hydrocarbons with less than stoichiometric oxygen for complete combustion occurs at very high temperature (1350°-1600° C.) and pressures up to 150 atm (Kirk and Othmer, Encyclopedea of Chemical Technology 3rd Edn., 1990 vol. 12 p. 952; Ullamann's Encyclopedea of Industrial Chemistry 5th Edn., 1989, vol. 12, p. 204). The main drawbacks of this process are as follows. This process is operated at a very high temperature and very high pressure and there is extensive soot or carbon formation, particularly from heavy hydrocarbons.

Recently, Ashcroft and co-workers (Nature, vol. 344, 1990, p. 319) have reported selective oxidation of methane to synthesis gas (which is a mildly exothermic reaction) using lanthanide ruthenium oxide (Ln₂ Ru₂ O₇ where Ln is lanthanide or rare earth element such as Pr, Sm, Eu, Gd, Tb, Dy, Tm, Yb, Lu) catalysts at 777° C. and total gas hourly space velocity of 4×10⁴ h⁻¹ with CH₄ /O₂ mole ratio of 2.0 and N₂ /CH₄ mole ratio of 2.0. The catalysts were prepared by conventional solid state reactions between Ln₂ O₃ and RuO₂ in a sealed silica tube. Although, high methane conversions to CO and H₂ have been obtained using these catalysts, the catalyst cost is exorbitantly high because of the use of extremely costly Ru in the catalyst in stoichiometric quantities (i.e. Ru/Ln mole ratio=1.0).

In view of the limitations of the prior art processes and catalysts used for the production of synthesis gas or (CO and H₂) from natural gas or methane, it was found desirable, during the course of the investigation leading to the present invention, to develop an improved process, which is not energy intensive (or highly endothermic), uses cheaper catalysts and operates at lower temperatures for the conversion of methane or natural gas to CO and H₂ or synthesis gas.

SUMMARY OF THE INVENTION

The main object of the present invention is to provide an improved process for the production of synthesis gas or CO and H₂ by oxidative conversion of natural gas or methane in the presence of free-oxygen using highly active/selective composite catalysts useful for oxidative conversion of natural gas or methane to synthesis gas or CO and H₂ in high yields. The catalysts contain non-transition and/or transition metal oxides, represented by the formula: T_(m).sup.. N_(n).sup.. R.sup.. O_(p) wherein T is a transition element selected from Ni, Co, Pd, Ru, Rh, Ir, Pt, Os, and Fe or the like or a mixture of two or more thereof; m the T/R mole ratio is from about 0.01 to 100, N is a transition or non-transition element selected from Ti, Zr, Hf, Y, Th, U, Zn, Cd, B, Al, Tl, Si, Sn, Pb, P, Sb, Bi, Mg, Ca, Sr, Ba, Ga, V, and Sc or the like or a mixture of two or more thereof, n the N/R mole ratio is from 0 to 100, R is a rare earth element selected from La, Ce, Pr, Nd, Pm, Sm, Eu, Gd, Tb, Dy, Ho, Er, Tm, Yb, and Lu or the like or a mixture of two or more thereof, O is oxygen and p is the number of oxygen atoms needed to fulfill the valence requirements of the elements in the composite catalyst.

Another important finding of the present invention is that, using the novel composite catalysts the oxidative conversion of natural gas or methane to synthesis gas or CO and H₂ in very high yields could be carried out at much lower temperatures and much higher gas hourly space velocities (or much lower contact times) than those used in the prior art. One more finding is that the above mentioned catalysts described in the present invention could be used with or without reduction, for the oxidative conversion of natural gas or methane to synthesis gas; the reduced catalysts could be operated in the process at lower temperatures. Whereas, the unreduced catalysts are first to be operated in the process at higher temperature and then could be used in the process at lower temperatures. The catalyst in its active form is essentially a reduced and/or partially reduced transition metal oxide dispersed in the matrix of other metal oxides.

The main finding of the present invention is that the synthesis gas (or H₂ and CO) can be produced in high yields and with a very high production rate by oxidative conversion of natural gas or methane to synthesis gas or H₂ and CO, which is a mildly exothermic reaction, using these novel composite catalysts.

DETAILED DESCRIPTION OF THE INVENTION

Accordingly, the present invention provides a process for the production of synthesis gas or CO and H₂ by oxidative conversion of natural gas or methane in the presence of free-oxygen using composite catalysts containing non-transition and/or transition metal oxides.

Accordingly, the present invention provides an improved process for production of synthesis gas or CO and H₂ by oxidative conversion of natural gas or methane which comprises passing continuously a gaseous reactant mixture comprising methane (or natural gas) and oxygen (or air) with or without water vapor over reduced or unreduced composite catalysts containing non-transition and/or transition metal oxides, represented by the formula: T_(m).sup.. N_(n).sup.. R.sup.. O_(p) wherein T is a transition element selected from Ni, Co, Pd, Ru, Rh, Ir, Pt, Os and Fe or the like or a mixture of two or more thereof, m the T/R mole ratio is from 0.01 to 100, N is a transition or non-transition element selected from Ti, Zr, Hf, Y, Th, U, Zn, Cd, B, A1, T1, Si, Sn, Pb, P, Sb, Bi, Mg, Ca, Sr, Ba, Ga, V and Sc or the like or a mixture of two or more thereof, n the N/R mole ratio is from 0 to 100, R is a rare earth element selected from La, Ce, Pr, Nd, Pm, Sm, Eu, Gd, Tb, Dy, Ho, Er, Tm, Yb and Lu or the like or a mixture of two or more thereof, O is oxygen and p is the number of oxygen atoms required to fulfill the valence requirement of the elements in the composite catalyst, in a fixed bed reactor at specified process conditions to produce gaseous products comprising carbon monoxide, hydrogen, carbon dioxide and water vapors, and separating the water vapors, unconverted reactants and feed components other than the reactants and carbon dioxide from the product stream by known methods.

The process operating conditions for the production of synthesis gas or CO and H₂ from natural gas or methane are as follows.

    ______________________________________                                         Pressure          0.5-50 atm.                                                  Reaction temperature                                                                             200°-1000° C.                                                    (preferably 250°-900° C.)                      Gas hourly space velocity                                                                        10.sup.3 -10.sup.8 cm.sup.3 · g.sup.-1                                · h.sup.-1                                                            (preferably 1 × 10.sup.4 - 5 ×                                     10.sup.6 cm.sup.3 · g.sup.-1 ·                               h.sup.-1)                                                    Concentration of CH.sub.4 in feed                                                                10-90 mole %                                                                   (preferably 20-80 mole %)                                    Concentration of O.sub.2 in feed                                                                 1-40 mole %                                                                    (preferably 10-36 mole %)                                    CH.sub.4 (or natural gas)/O.sub.2                                                                1.6-10                                                       mole ratio in feed                                                                               (preferably 1.8-4)                                           Concentration of N.sub.2 or Ar                                                                   0-60 mole %                                                  or their mixture in feed                                                       Concentration of water in                                                                        0-65 mole %                                                  feed                                                                           H.sub.2 O/CH.sub.4 (or natural gas)                                                              0-3 (preferably 0-2)                                         mole ratio in feed                                                             Concentration of CO.sub.2 in feed                                                                0-10 mole %                                                  Concentration of C.sub.2 H.sub.6 in feed                                                         0-10 mole %                                                  Concentration of C.sub.3 and C.sub.4                                                             0-5 mole %                                                   alkanes in feed                                                                ______________________________________                                    

The catalyst is prepared as follows: (i) mixing thoroughly finely ground one or more transition metal compounds represented by the formula: R.X_(a) wherein T is a transition element selected from Ni, Co, Pd, Ru, Rh, Ir, Pt, Os and Fe or the like or a mixture of two or more thereof; X is selected from NO₃, CH₃ COO, OH, O, CO₃, Cl, and oxalate anions, or the like and a is number of X required to fulfill the valence requirement of the transition element T in the compound; one or more finely ground rare earth metal compounds, represented by the formula: R.Y_(b), wherein R is a rare earth element selected from La, Ce, Pr, Nd, Pm, Sm, Eu, Gd, Tb, Dy, Ho, Er, Tm, Yb, and Lu or the like or a mixture of two or more thereof, Y is selected from NO₃, OH, O, CO₃, Cl, CH₃ COO and oxalate anions or the like, and b is the number of Y required to fulfill the valence requirement of the rare earth element, and, if required, one or more finely ground non-transition or transition metal compounds represented by a formula: N.Y_(b), wherein N is selected from non-transition elements such as Mg, Ca, Zn, Cd, B, Al, Tl, Si, Sn, Pb, P, Sb, Bi, Sr, Ba and Ga, or the like or from transition elements such as Ti, Zr, Hf, Y, Th, U, V, and Sc, or the like, which are catalyst precursors; with the T/R and N/R mole ratios of about 0.01 to 100 and 0 to 100, respectively, with or without water, if water is used, the water is just sufficient to make a thick paste, (ii) heating the mixture of catalyst precursors to dryness at a temperature of about 80°-250° C. in air, (iii) decomposing the dried mass containing catalyst precursors to their oxides at a temperature of about 400°-1500° C. in the presence of air or inert gas (viz. N₂, He, Ar or the like) or under vacuum for about 0.1-50 h, (iv) powdering the decomposed mass and making by known methods catalyst pellets, extrudes or granules of required size, and (v) calcining the catalyst bodies at a temperature of about 400°-1500° C. in the presence of air, inert gas (viz. N₂, He, Ar or like), CO₂, or their mixtures, or under vacuum for about 0.1-100 h.

The preferred transition element, T, in the catalyst or in the mixture of catalyst precursors is Ni or Co or a mixture of two or more therof. The preferred rare earth element R in the catalyst or in the mixture of catalyst precursors is Yb, Eu, Sm, Nd, Pr, Dy, or La or a mixture of two or more thereof. The preferred element, N, in the catalyst or in the mixture of catalyst precursors is Al, Mg, or Ca, or a mixture of two or more thereof. The preferred T/R mole ratio m in the catalyst or in the mixture of catalyst precursors is in the range of 0.1-10. The preferred N/R mole ratio n in the catalyst or in the mixture of catalyst precursors is in the range of 0-10. The preferred temperature for the decomposition of the catalyst precursors is in the range of 500°-1000° C. The preferred period of decomposition of catalyst precursors in 0.5-20 h. The preferred temperature for calcination of the catalyst is in the range of 500°-1000° C. The preferred period of calcination of the catalyst is 0.5-20 h. The preferred gas atmosphere for the decomposition of catalyst precursors or the catalyst calcination is air or inert gas.

The product obtained from the process of the invention is a novel composite catalyst containing non-transition and/or transition metal oxides, useful for oxidative conversion of natural gas or methane to synthesis gas or CO and H₂.

The present invention reveals that the composite catalysts, containing non-transition and/or transition metal oxides, showing very high methane conversion activity, very high activity/selectivity for CO and H₂ or synthesis gas formation, very high productivity for CO and H₂ and long catalyst life in the oxidative conversion of methane (or natural gas) to CO and H₂ (or synthesis gas), operating at extremely high space velocities and at both lower (below 700° C., even at about 300° C.) and higher (above 700° C.) temperatures, can be prepared by the catalyst preparation process described. Using these catalysts, the oxidative conversion of methane or natural gas to CO and H₂ or synthesis gas can be carried out at much lower temperatures. The chemicals used in the catalyst preparation are cheaper.

Using the composite catalyst prepared by this process for oxidative conversion of methane (or natural gas) in presence of free oxygen (i.e. gaseous oxygen), methane can be converted at about 300°-900° C. to CO and H₂ (or synthesis gas) at a very high conversion (60-100%) with very high selectivity (80-100%) and productivity (about 5-15 mol. g⁻¹. h⁻¹ for CO and about 10-30 mol. g⁻¹. h⁻¹ for H₂) ) giving H₂ /CO mole ratio in the products about 2.0±0.3 without loss of catalytic activity/selectivity for a long period. For example, NiO-Yb₂ O₃ catalyst (with Ni/Yb mole ratio=1.0) gave 73% conversion of methane with above 86% selectivity for CO and H₂ (H₂ /CO mole ratio=2.0) and productivity of about 10 and 20 mols per gram catalyst per hour for CO and H₂, respectively, in the oxidative conversion of methane to synthesis gas at 399° C. and gas hourly space velocity of 515,000 cm³. g^(-h).sup..h⁻¹.

The catalyst may or may not be reduced before the catalytic reaction. The catalyst reduction may be carried out by passing continuously a gaseous mixture comprising hydrogen and inert gas (i.e., N₂, He, or Ar) over the catalyst in the fixed bed reactor at the following conditions.

    ______________________________________                                         Catalyst reduction pressure                                                                         1-5 atm.                                                  Catalyst reduction temperature                                                                      300°-700° C.                                Concentration of H.sub.2 in reducing                                                                1-100 mole %                                              gas mixture                                                                    Space velocity of reducing gas                                                                      10.sup.3 -10.sup.5 cm.sup.3 · g.sup.-1                                · h.sup.-1                                       mixture                                                                        Catalysts reduction period                                                                          0.5-20 h                                                  ______________________________________                                    

When the catalyst is not reduced by hydrogen before the catalytic reaction, the reduction of the catalyst can be effected by passing the reaction mixture comprising methane (or natural gas) and oxygen (or air) over the catalyst at temperature in the range of 500°-900° C. for a period in the range of 0.1-10 h. Unless the catalyst is reduced this way or by hydrogen as described above, the catalytic oxidative conversion of methane to synthesis gas over the catalyst does not occur at lower temperatures (below 500° C.); the catalyst reaction on the unreduced catalyst occurs above 500° C. The unreduced catalyst is reduced during the catalytic reaction above 500° C. and then the process could be operated at lower temperatures.

In the said process, the products formed are carbon monoxide (CO) and hydrogen (H₂) as major products and water and carbon dioxide (CO₂) as minor products. The gaseous product stream comprises the above mentioned products, unconverted reactants (i.e. methane or natural gas and oxygen) and components of feed other than reactants.

Because of addition of water in the feed, the H₂ /CO mole ratio in the product is increased by the shift reaction: CO+H₂ O⃡H₂ +CO₂, occurring simultaneously with the oxidative conversion of methane (or natural gas) to CO and H₂ or synthesis gas.

The present invention reveals that methane or natural gas can be converted to CO and H₂ or synthesis gas in high yields with very high productivity at both the lower (at below 700° C. and even at about 300° C.) and the higher (at above 700° C.) temperatures by the said process described above. In the said process of the invention, at 300°-900° C., the conversion of methane or natural gas, is as high as 60-100% with 80-100% selectivity for CO and H₂ and productivity of CO and H₂ as high as 10-30 mol. g⁻¹ h⁻¹ and 20-60 mol g⁻¹. h⁻¹, respectively, can be achieved.

The main advantages of the invention are

(i) The process of the present invention involves oxidative conversion of natural gas or methane to synthesis gas or co or H₂, which is a mildly exothermic reaction, and hence the process is not energy intensive. After start of the catalytic reaction, there is no need to provide energy for the reaction as heat is generated during the reaction.

(ii) Synthesis gas could be produced by the process of the present invention in high yields with very high production rate at much lower temperatures than that used in the processes known in the prior art.

(iii) The process of the present invention uses a novel composite catalyst containing transition elements (preferably Ni, Co or their mixture), which are much cheaper than catalysts containing costly noble metals like ruthenium, in stoichiometric quantities with other elements used in the processes known in the prior art.

(iv) The composite catalysts of the present invention show high activity/selectivity at extremely high space velocities (i.e at very low contact times) and hence have very high productivity for both CO and H₂ in the oxidative conversion of methane or natural gas to synthesis gas. There is no carbon deposition on the catalyst in the oxidative conversion of methane (or natural gas) to CO and H₂ or synthesis gas. In the process of the present invention, the H₂ /CO mole ratio in the product gas is about 2.0 and, if required, it can be increased above 2.0 by adding water vapors in the feed.

The present invention is described with respect to the following examples. These are provided for illustrative purpose only and not to be construed as limitations on the invention.

Definition of terms used in the Examples ##EQU1##

Productivity (or space-time-yield) for a particular product is the amount of the product formed in the process per unit weight of catalyst per unit time.

Gas hourly space velocity (GHSV) is the volume of gaseous reactant mixture (measured at STP) passed over a unit weight of catalyst per hour.

In the conversion of natural gas, the selectivity and conversion data are based on the carbon balance.

EXAMPLE-1

Preparation of NiO-Yb₂ O₃ catalyst (with Ni/Yb mole ratio=1.0).

Finely ground 7.0 g of Yb₂ O₃, finely ground 10.34 g of Ni(NO₃)₂.sup.. 6H₂ O and 1.0 ml of deionized water are thoroughly mixed and the resulting thick paste is dried in air oven at 120° C. for 6 h. The dried mass is decomposed at 605° C. in air for 4 h. The decomposed mass is then powdered, pressed binder-free at 4 ton pressure and crushed to 20-30 mesh size particles. The catalyst particles are then calcined in air at 900° C. for 4 h to provide the desired NiO-Yb₂ O₃ catalyst. The surface area of the catalyst was 6.30 m². g⁻¹.

EXAMPLE-2

Preparation of NiO-CoO-Yb₂ O₃ catalyst (Ni:Co:Yb=1:0.5:0.5).

Finely ground 9.74 g of Co(NO₃)₂ 6H₂ O, finely ground 6.60 g of Yb₂ O₃, finely ground 19.46 g of nickel nitrate hexahydrate and 4 ml of deionized water are thoroughly mixed and the resulting mixture is dried in air oven at 120° C. for 6 h. The dried mass is then decomposed at 610° C. in air for 6 h. The decomposed solid mass is then powdered, pressed binder-free at 4 (or 5) ton pressure and crushed to particles of 22-30 mesh. The catalyst particles are then calcined in air at 930° C. for 6 h to provide the desired NiO-CoO-Yb₂ O₃ catalyst. The surface area of the catalyst was 3.26 m² g⁻¹.

EXAMPLE-3

Preparation of NiO-MgO-Sm₂ O₃ catalyst (Ni:Mg:Sm=1:1:0.1).

Finely ground 19.46 g of Ni(NO₃)₂.sup.. 6H₂ O, finely ground 6.25 g of magnesium carbonate, finely ground 2.55 g of (CH₃ CO₂)₃ Sm.sup.. 3H₂ O and 7 ml of deionized water are thoroughly mixed and the resulting mixture is dried in air oven at 120° C. for 4 h. The dried mass is decomposed in air at 630° C. for 4 h. The decomposed mass is then powdered, pressed binder-free at 5 ton pressure and crushed to 22-30 mesh size particles. The catalyst particles are then calcined in air at 930° C. for 5 h to provide the desired NiO-MgO-Sm₂ O₃ catalyst. The surface area of the catalyst was 13.4 m². g⁻¹.

EXAMPLE-4

Preparation of NiO-Al₂ O₃ -Yb₂ O₃ catalyst (Ni:Al:Yb=1:1:1).

Finely ground 5.84 g of Ni(NO₃)₂.sup.. 6H₂ O, finely ground 2.05 g of Al₂ O₃, finely ground 7.91 g of Yb₂ O₃ in 2 ml of deionized water are thoroughly mixed and the resulting mixture is dried in air oven at 120° C. for 6 h. The dried mass is then decomposed at 600° C. in air for 6 h. The decomposed mass is then powdered, pressed binder-free at 5 ton pressure and crushed to 22-30 mesh size particles. The catalyst particles are then calcined in presence of air at 900° C. for 6 h to provide the desired NiO-Al₂ O₃ -Yb₂ O₃ catalyst. The surface area of the catalyst was 19.08 m². g⁻¹.

EXAMPLE-5

Process for the oxidative conversion of methane to CO and H₂ (or synthesis gas) using the NiO-Yb₂ O₃ (Ni/Yb mole ratio=1.0) catalyst, the preparation of which is described in Example-1.

The oxidative conversion of methane to CO and H₂ (i.e. synthesis gas) over the catalyst was carried out in a flow quartz reactor (i.d=5 mm) packed with the catalyst particles (20 mg) using a mixture of pure methane and oxygen as a feed. The reactor temperature was measured by Chromel-Alumel thermocouple located in the catalyst bed. The reactor effluent gases were cooled at about 0° C. to condense the water formed in the reaction using coiled condenser immersed in ice - water slurry and then analyzed for CO, CO₂, H₂ and unconverted methane and O₂ by an on-line gas chromatograph using a Spherocarb column. The change in the volumetric flow rate of gases due to the reaction (CH₄ +1/2O₂ CO+2 H₂) was determined by measuring the flow rate of feed and product gases (after removing water) using soap bubble flow-meter. Before carrying out the reaction, the catalyst was pretreated in situ at the calcination temperature of the catalyst in a flow of pure N₂ (50.0 ml.min⁻¹) for 1 h.

The process performance was evaluated at the following reaction conditions.

    ______________________________________                                         Feed composition                                                                              67 mol % methane and 33 mol % O.sub.2                           Gas hourly space velocity                                                                     (5.16 ± 0.20) × 10.sup.5                               (GHSV)         cm.sup.3 · g.sup.-1 · h.sup.-1                Pressure       1.2 ± 0.1 atm.                                               ______________________________________                                    

reaction was carried out first at 602° C. for about 1 h and then at the other temperatures.

The results obtained at different reaction temperatures are as follows.

    ______________________________________                                                      Reaction temperature (°C.)                                              602  702     803     496   298                                    ______________________________________                                         Total CH.sub.4 conversion (%)                                                                 80.6   84.9    89.3  74.0  71.1                                 Selectivity for CO (%)                                                                        92.6   95.2    97.4  89.8  84.4                                 Selectivity for H.sub.2 (%)                                                                   93.1   95.7    96.3  90.0  87.9                                 Productivity for CO                                                                           9.3    10.8    12.0  7.6   6.6                                  (mol. g.sup.-1 h.sup.-1)                                                       Productivity for H.sub.2                                                                      18.7   21.4    23.7  15.2  13.9                                 (mol. g.sup.-1 h.sup.-1)                                                       H.sub.2 /CO mole ratio                                                                        2.01   1.98    1.98  2.00  2.08                                 in the product                                                                 ______________________________________                                    

EXAMPLE-6

Process for the oxidative conversion of methane to CO and H₂ (or synthesis gas) over the NiO-Yb₂ O₃ (Ni/Yb mole ratio=1.0) catalyst, the preparation of which is described in Example-1, reduced by hydrogen before the catalytic reaction.

The reaction over the catalyst was carried out in the reactor and by the procedure similar to that described in Example-5 except that the catalyst pretreated in situ was reduced in the flow (60 cm³. min⁻¹) of a mixture of H₂ and N₂ (20% H₂) at 500° C. for a period of 1 h, before carrying out the catalytic reaction. The reaction was carried out at the following conditions.

    ______________________________________                                         Feed composition                                                                               67 mol % CH.sub.4 and 33 mol % O.sub.2                         Gas hourly space velocity                                                                      518,000 cm.sup.3 · g.sup.-1 · h.sup.-1       (GHSV)                                                                         Pressure        1.2 atm.                                                       ______________________________________                                    

The results obtained are given below.

    ______________________________________                                                        Reaction temperature (°C.)                                              500  603      705    399                                        ______________________________________                                         Total CH.sub.4 conversion (%)                                                                   76.7   81.3     85.1 73.0                                     Selectivity for CO (%)                                                                          88.9   93.2     94.9 86.2                                     Selectivity for H.sub.2 (%)                                                                     88.1   89.3     91.7 86.3                                     H.sub.2 /CO mole ratio                                                                          1.98   1.92     1.93 2.00                                     in the product                                                                 ______________________________________                                    

EXAMPLE-7

Process for the oxidative conversion of natural gas to CO and H₂ (or synthesis gas) over the reduced NiO-Yb₂ O₃ (Ni/Yb mole ratio=1.0) catalyst, the preparation of which is described in Example-1.

The reaction over the catalyst was carried out in the reactor and by the procedure similar to that described in Example-6 except that, instead of methane, natural gas comprising of methane, ethane and C₃ and C₄ alkanes is used in the feed, at the following process conditions.

    ______________________________________                                         Feed composition                                                                             59.6 mol % CH.sub.4, 6.0 mol % C.sub.2 H.sub.6,                                1.4 mol % C.sub.3 and C.sub.4 alkanes,                                         32 mol % O.sub.2, 0.3 mol % CO.sub.2 and                                       0.7 mol % N.sub.2                                                GHSV          515,000 cm.sup.3 · g.sup.-1 · h.sup.-1         Pressure      1.08 atm.                                                        ______________________________________                                    

The results obtained at different temperatures are as follows.

    ______________________________________                                                         Reaction temperature (°C.)                                              502     651    801                                             ______________________________________                                         Total carbon conversion (%)                                                                      76.3      84.9   93.6                                        Selectivity for CO (%)                                                                           90.8      93.2   98.5                                        Selectivity for H.sub.2 (%)                                                                      85.5      92.6   97.6                                        H.sub.2 /CO mole ratio                                                                           1.88      1.99   1.98                                        in products                                                                    ______________________________________                                    

EXAMPLE-8

Process for the oxidative conversion of methane to synthesis gas using the NiO-Yb₂ O₃ catalyst, the preparation of which is described in Example-1, at different gas hourly space velocities.

The catalytic process was carried out in the reactor and by the procedure similar to that described in Example-5 at the following reaction conditions.

    ______________________________________                                         Feed composition                                                                              67 mol % CH.sub.4 and 33 mol % O.sub.2                          Pressure       1.4 ± 0.1 atm.                                               ______________________________________                                    

The results at different reaction temperatures are as follows.

    ______________________________________                                         GHSV (cm.sup.3 · g.sup.-1 · h.sup.-1)                                       121,800 516,000    10,32,000                                    Reaction temperature (°C.)                                                             703     702    496   698  501                                   ______________________________________                                         Total CH.sub.4 conversion (%)                                                                 86.5    84.9   74.0  83.9 72.7                                  Selectivity for CO (%)                                                                        92.8    95.2   89.8  96.1 91.1                                  Selectivity for H.sub.2 (%)                                                                   94.6    95.7   90.3  93.7 90.3                                  Productivity for CO                                                                           2.5     10.6   7.6   20.6 14.8                                  (mol. g.sup.-1 · h.sup.-1)                                            Productivity for H.sub.2                                                                      5.2     21.3   15.2  40.9 29.3                                  (mol. g.sup.-1 · h.sup.-1)                                            H.sub.2 /CO mole ratio                                                                        2.04    2.01   2.01  1.95 1.98                                  in products                                                                    ______________________________________                                    

EXAMPLE-9

This example illustrates the process for oxidative conversion of methane to synthesis gas using NiO-CoO-Yb₂ O₃ catalyst, the preparation of which is described in Example-2, at different process conditions. The reaction over the catalyst was carried out in the reactor and by the procedure similar to that described in Example-5, using a mixture of pure methane and O₂ as a feed. The results at different process conditions are presented in Table-1.

                                      TABLE 1                                      __________________________________________________________________________     Results on the oxidative conversion of methane to synthesis gas over the       NiO--CoO--Yb.sub.2 O.sub.3                                                     Catalyst, preparatiaon of which is described in Example-2, at different        process conditions.                                                                                   CH.sub.4          H.sub.2 /CO                                                                        Productivity                      Temp.                                                                              CH.sub.4 /O.sub.2                                                                   GHSV     Pressure                                                                            Conversion                                                                           Selectivity                                                                          Selectivity                                                                          mole                                                                               (mol. g.sup.-1 ·                                                      h.sup.-1)                         (°C.)                                                                       ratio                                                                               (cm.sup.3 · g.sup.-1 · h.sup.-1)                                      (atm)                                                                               (%)   for CO (%)                                                                           for H.sub.2 (%)                                                                      ratio                                                                              for CO                                                                             for H.sub.2                   __________________________________________________________________________     703 2.0  5, 16, 000                                                                              1.115                                                                               84.7  94.2  94.0  2.00                                                                               10.5                                                                               21.0                          803 2.0  5, 16, 000                                                                              1.20 90.9  95.8  95.7  2.00                                                                               12.4                                                                               24.8                          500 4.0  5, 16, 000                                                                              1.065                                                                               30.0  79.7  90.6  2.27                                                                               1.1 2.5                           703 4.0  5, 16, 000                                                                              1.070                                                                               37.0  92.0  97.2  2.11                                                                               1.9 4.1                           500 8.0  5, 16, 000                                                                              1.055                                                                               14.8  68.3  90.0  2.64                                                                               0.2 0.6                           705 8.0  5, 16, 000                                                                              1.065                                                                               20.9  90.8  96.3  2.12                                                                               0.6 1.3                           603 2.0  1, 12, 500                                                                              1.045                                                                               71.1  83.3  89.1  2.14                                                                               1.4 3.0                           702 2.0  1, 12, 500                                                                              1.075                                                                               80.2  90.0  92.1  2.05                                                                               1.9 4.0                           500 2.0  1, 12, 500                                                                              1.095                                                                               68.5  79.5  84.0  2.11                                                                               1.3 2.6                           700 2.0  11, 35, 200                                                                             1.255                                                                               69.6  93.9  87.7  1.87                                                                               14.8                                                                               27.8                          505 2.0  11, 35, 200                                                                             1.22 65.5  90.3  86.5  1.92                                                                               13.0                                                                               24.9                          __________________________________________________________________________

EXAMPLE-10

This example illustrates the process for the oxidative conversion of methane to CO and H₂ (or synthesis gas) using the NiO-CoO-Yb₂ O₃ catalyst, the preparation of which is given in Example-2, reduced before the reaction at 500° C. and 600° C.

The catalytic process was carried out in the reactor and by the procedure similar to that described in Example-6, at the following process conditions.

    ______________________________________                                         Feed composition                                                                               66 mol % CH.sub.4 and 34 mol % O.sub.2                         Gas hourly space velocity                                                                      515,000 cm.sup.3 · g.sup.-1 · h.sup.-1       (GHSV)                                                                         Pressure        1.7 atm.                                                       ______________________________________                                    

The catalyst was reduced before carrying out the reaction at 500° C. and 600° C. by a mixture of H₂ and N₂ (20% H₂) for 1 h.

The results obtained in the process using the catalyst reduced at 500° C. and 600° C. are as follows.

    ______________________________________                                                Catalyst reduction                                                             temperature (°C.)                                                Reaction                                                                       temperature                                                                             500             600                                                   (°C.)                                                                            503    703    603  385  401  500  600  702                            ______________________________________                                         Total CH.sub.4 -                                                                        67.5   77.3   73.0 63.8 73.9 78.5 77.6 84.8                           conversion                                                                     (%)                                                                            Selectivity                                                                             90.2   95.5   92.2 86.2 88.2 91.4 91.9 95.3                           for CO (%)                                                                     Selectivity                                                                             90.6   93.0   92.6 88.6 88.4 90.2 90.1 93.1                           for H.sub.2 (%)                                                                H.sub.2 /CO mole                                                                        2.01   1.95   2.01 2.06 2.00 1.97 1.96 1.95                           ratio                                                                          ______________________________________                                    

EXAMPLE-11

This example illustrates the process for the oxidative conversion of methane to synthesis gas (CO and H₂) using the NiO-CoO-Yb₂ O₃ catalyst, the preparation of which is given in Example-2, at different H₂ O/CH₄ mole ratios in the feed.

The catalytic process was carried out in the reactor and by the procedure similar to that described in Example-5, using a mixture of CH₄, O₂ and water vapors as a feed at the following reaction conditions.

    ______________________________________                                         CH.sub.4 /O.sub.2 mole ratio in feed:                                                              2.0                                                        Pressure:           1.1 to 1.2 atm.                                            Gas hourly space velocity:                                                                         (5.4 + 0.3) × 10.sup.5                               (GHSV)              cm.sup.3 · g.sup.-1 · h.sup.-1           ______________________________________                                    

The results obtained at different H₂ O/CH₄ mole ratios in feed and reaction temperatures are given below.

    __________________________________________________________________________     Reaction temperature (°C.)                                                           704                                                                               700 500                                                                               500                                                                               700                                                                               702 500                                                                               700                                        H.sub.2 O/CH.sub.4 mole ratio                                                               0.0                                                                               0.22                                                                               0.22                                                                              0.58                                                                              0.58                                                                              0.87                                                                               0.87                                                                              1.9                                        __________________________________________________________________________     Total CH.sub.4 -                                                                            86.1                                                                              83.7                                                                               72.1                                                                              79.9                                                                              81.5                                                                              76.1                                                                               61.7                                                                              66.7                                       conversion (%)                                                                 Selectivity  95.0                                                                              85.8                                                                               76.6                                                                              66.0                                                                              72.0                                                                              67.1                                                                               55.9                                                                              44.5                                       for CO (%)                                                                     Selectivity  95.2                                                                              98.2                                                                               94.6                                                                              95.0                                                                              97.2                                                                              93.6                                                                               87.5                                                                              91.0                                       for H.sub.2 (%)                                                                H.sub.2 /CO mole                                                                            2.00                                                                              2.29                                                                               2.47                                                                              2.88                                                                              2.70                                                                              2.79                                                                               3.13                                                                              4.09                                       ratio                                                                          __________________________________________________________________________

EXAMPLE-12

This example illustrates the process for the oxidative conversion of methane to synthesis gas (CO and H₂) using the reduced NiO-MgO-Sm₂ O₃ (Ni:Mg:Sm=1:1:0.1) catalyst, the preparation of which is given in Example-3, at different reaction temperatures.

The catalytic process was carried out in the reactor and by the procedure similar to that described in Example-6, at the following conditions.

    ______________________________________                                         Feed composition: 67 mol % CH.sub.4 and                                                          33 mol % O.sub.2                                             Pressure:         1.1 atm.                                                     Gas hourly space velocity:                                                                       518,000 cm.sup.3 · g.sup.-1 ·                                h.sup.-1                                                     (GHSV)                                                                         ______________________________________                                    

The results obtained at the different reaction temperatures aer as follows.

    ______________________________________                                                        Reaction temperature (°C.)                                              602  507      701    326                                        ______________________________________                                         Total CH.sub.4 conversion (%)                                                                   76.8   69.1     81.7 61.9                                     Selectivity for CO (%)                                                                          92.0   86.7     95.0 79.2                                     Selectivity for H.sub.2 (%)                                                                     93.1   89.7     96.2 87.0                                     H.sub.2 /CO mole ratio                                                                          2.02   2.07     2.03 2.20                                     ______________________________________                                    

EXAMPLE-13

This example illustrates the use or performance of the NiO-Yb₂ O₃ catalyst, the preparation of which is described in Example-1, for the oxidative conversion of methane to synthesis gas.

The oxidative conversion of methane to synthesis gas (i.e. CO and H₂ over the catalyst was carried out in a flow quartz reactor (i.d=5 mm) packed with the catalyst particles (20 mg) using a mixture of pure methane and oxygen as a feed. The reactor temperature was measured by Chromel-Alumel thermocouple located in the catalyst bed. The reactor effluent gases were cooled at about 0° C. to condense the water formed in the reaction using coiled condenser immersed in ice-water slurry and then analyzed for CO, CO₂, H₂ and unconverted methane and O₂ by an on-line gas chromatograph using a Spherocarb column. The change in the volumetric flow rate of gases due to the reaction (CH₄ +1/2O CO+2H₂) was determined by measuring the flow rate of feed and product gases (after removing water), using soap bubble flow-meter. Before carrying out the reaction, the catalyst was pretreated in situ at the calcination temperature of the catalyst in a flow of pure N₂ (50.0 ml.min⁻¹) for 1 h and then reduced in the flow (60 cm³. min⁻¹) of a mixture of H₂ and N₂ (20% H₂) at 500° C. for 1 h.

The catalyst performance was evaluated at the following process conditions.

    ______________________________________                                         Feed composition: 67 mol % methane and                                                           33 mol % O.sub.2                                             Space velocity:   515,000 cm.sup.3 · g.sup.-1 ·                                h.sup.-1                                                     Pressure:         1.2 atm.                                                     ______________________________________                                    

The results obtained at different reaction temperatures are as follows.

    ______________________________________                                                        Reaction temperature (°C.)                                              703  603      500    399                                        ______________________________________                                         Total CH.sub.4 conversion (%)                                                                   85.7   81.3     76.7 73.0                                     Selectivity for CO (%)                                                                          94.4   93.2     88.9 86.2                                     Selectivity for H.sub.2 (%)                                                                     91.7   92.4     88.1 86.3                                     Productivity for CO                                                                             12.5   11.4     10.5 9.7                                      (mol · g.sup.-1 · h.sup.-1)                                  Productivity for H.sub.2                                                                        24.2   22.6     20.8 19.7                                     (mol · g.sup.-1 · h.sup.-1)                                  H.sub.2 /CO mole ratio                                                                          1.94   1.98     1.98 2.00                                     in the product                                                                 ______________________________________                                    

EXAMPLE-14

The use and stability of the NiO-Yb₂ O₃ catalyst, the preparation of which is described in Example-1, in the oxidative conversion of methane to synthesis gas.

The reaction over the catalyst was carried out in the reactor and by the procedure similar to that described in Example-13, at the following process conditions.

    ______________________________________                                         Feed Composition:                                                                              67 mol % CH.sub.4 and 33 mol % O.sub.2                         Gas hourly space velocity:                                                                     516,000 cm.sup.3 · g.sup.-1 · h.sup.-1       (GHSV)                                                                         Pressure:       1.2 atm.                                                       Reaction temperature:                                                                          600 ± 3° C.                                          ______________________________________                                    

The results showing the time-on-stream activity/selectivity of the catalyst in the process are given below.

    ______________________________________                                                      Time - on - stream (h)                                                         0.5  4.0    6.0    8.0  12.0 16.0                                 ______________________________________                                         Total CH.sub.4 conversion (%)                                                                 80.6   81.3   80.7 82.5 81.1 81.9                               Selectivity for CO (%)                                                                        93.6   93.2   93.7 93.1 94.6 94.3                               Selectivity for H.sub.2 (%)                                                                   92.1   92.4   92.5 91.9 92.7 92.9                               H.sub.2 /CO mole ratio                                                                        1.96   1.98   1.97 1.97 1.96 1.97                               in products                                                                    ______________________________________                                    

EXAMPLE-15

Use of the NiO-Yb₂ O₃ catalyst, the preparation of which is described in Example-1, without its reduction by H₂, in the oxidative conversion of methane to synthesis gas.

The reaction over the catalyst was carried out in the reactor and by the procedure similar to that described in Example-13 except that the catalyst pretreated in situ was not reduced by H₂ before carrying out the catalytic reaction. The reaction was carried out at the following conditions.

    ______________________________________                                         Feed composition:                                                                              67 mol % CH.sub.4 and 33 mol % O.sub.2                         Gas hourly space velocity:                                                                     515,000 cm.sup.3 · g.sup.-1 · h.sup.-1       (GHSV)                                                                         Pressure:       1.35 atm.                                                      ______________________________________                                    

The results obtained at different reaction temperatures are given below.

    ______________________________________                                                        Reaction temperature (°C.)                                              700  603      496    298                                        ______________________________________                                         Total CH.sub.4 conversion (%)                                                                   84.9   79.1     74.0 71.1                                     Selectivity for CO (%)                                                                          95.2   93.0     89.8 84.4                                     Selectivity for H.sub.2 (%)                                                                     95.7   91.6     90.0 87.9                                     H.sub.2 /CO mole ratio in                                                                       2.01   1.97     2.00 2.08                                     product                                                                        ______________________________________                                    

EXAMPLE-16

Use of the NiO-CoO-Yb₂ O₃ catalyst, the preparation of which is described in Example-2, for the oxidative conversion of methane to synthesis gas. The reaction over the catalyst was carried out in the reactor and by the procedure similar to that described in Example-13, at the following reaction conditions.

    ______________________________________                                         Feed composition:                                                                              67 mol % CH.sub.4 and 33 mol % O.sub.2                         Gas hourly space velocity:                                                                     517,000 cm.sup.3 · g.sup.-1 · h.sup.-1       (GHSV)                                                                         Pressure:       1.09 atm.                                                      ______________________________________                                    

The results obtained at the different reaction temperatures are as follows.

    ______________________________________                                                        Reaction temperature (°C.)                                              703  603      502    385                                        ______________________________________                                         Total CH.sub.4 conversion (%)                                                                   77.3   73.0     65.8 63.8                                     Selectivity for CO (%)                                                                          95.5   92.2     90.1 86.2                                     Selectivity for H.sub.2 (%)                                                                     93.1   92.6     90.3 88.6                                     H.sub.2 /CO mole ratio                                                                          1.95   2.01     2.00 2.06                                     ______________________________________                                    

EXAMPLE-17

Use of NiO-CoO-Yb₂ O₃ catalyst (Ni:Co:Yb=1:0.5:0.5), prepared by the procedure similar to that described in Example-2 except the fact that the catalyst calcination temperature was 600° C., in the oxidative conversion of methane to synthesis gas. The surface area of the catalyst was 23.9 m². g⁻¹.

The reaction over the catalyst was carried out in the reactor and by the procedure similar to that described in Example-13, at the following conditions.

    ______________________________________                                         Feed composition:                                                                              66 mol % CH.sub.4 and 34 mol % O.sub.2                         Gas hourly space velocity:                                                                     515,000 cm.sup.3 · g.sup.-1 · h.sup.-1       (GHSV)                                                                         Pressure:       1.35 atm.                                                      ______________________________________                                    

the results obtained at different reaction temperatures are as folllows.

    ______________________________________                                                            Reaction temperature (°C.)                                              605  502                                                    ______________________________________                                         Total CH.sub.4 conversion (%)                                                                       86.0   84.5                                               Selectivity for CO (%)                                                                              92.4   91.7                                               Selectivity for H.sub.2 (%)                                                                         93.5   91.9                                               H.sub.2 /CO mole ratio                                                                              2.02   2.0                                                ______________________________________                                    

EXAMPLE-18

Preparation of NiO-Eu₂ O₃ catalyst with Ni/Eu mole ratio of 1.0.

Finely ground 12.0 g of Eu₂ O₃, finely ground 19.8 g of Ni(NO₃)₂.sup.. 6H₂ O and 4 ml of deionized water are thoroughly mixed and resulting mixture is heated in air oven at 100° C. for 4 h and then decomposed at 605° C. in air for 6 h. The decomposed solid mass is then powdered, pressed binder-free at 5 ton pressure and crushed to 22-30 mesh size particles. The catalyst particles are then calcined at 925° C. in presence of air for 4 h to provide the desired NiO-Eu₂ O₃ catalyst. The surface area of the catalyst was 5.60 m². g⁻¹.

EXAMPLE-19

Preparation of NiO-Eu₂ O₃ catalyst with Ni/Eu mole ratio of 0.1.

Finely ground 12.0 g of Eu₂ O₃, finely ground 2.0 g of nickel nitrate hexahydrate and 8 ml of deionized water are thoroughly mixed and the resulting paste is dried in air oven at 120° C. for 6 h. The dried mass is then decomposed at 610° C. in air for 4 h. The decomposed solid mass is then powdered, pressed binder-free at 4 ton pressure and crushed to particles of 22-30 mesh. The catalyst particles are then calcined in air at 910° C. for 10 h to provide the desired NiO-Eu₂ O₃ catalyst. The surface area of the catalyst was 1.80 m². g⁻¹.

EXAMPLE-20

Preparation of NiO-Yb₂ O₃ catalyst with Ni/Yb mole ratio of 4.0.

Finely ground 12.0 g of Yb₂ O₃, finely ground 70.84 g of Ni(NO₃)₂.sup.. 6H₂ O, of and 6 ml of deionized water are thoroughly mixed and the resulting thick paste is dried in air oven at 120° C. for 6 h. The dried mass is decomposed in air at 600° C. for 6 h. The decomposed mass is then powdered, pressed binder-free at 4 ton pressure and crushed to 22-30 mesh size particles. The catalyst particles are then calcined in air at 910° C. for 5 h to provide the desired NiO-Yb₂ O₃ catalyst. The surface area of the catalyst was 5.88 m². g⁻¹.

EXAMPLE-21

Preparation of NiO-Sm₂ O₃ catalyst with Ni/Sm mole ratio of 1.0.

Finely ground 7.62 g of Ni(NO₃)₂.6H₂ O, finely ground 10.0 g of (CH₃ CO₂)₃ Sm.sup.. 3H₂ O and 2 ml of deionized water are thoroughly mixed and the resulting paste is dried in air oven at 130° C. for 12 h. The dried mass is then decomposed in air at 605° C. for 4 h. The decomposed mass is then powdered, pressed binder-free at 5 ton pressure and crushed to 22-30 mesh size particles. The catalyst particles are then calcined in presence of air at 930° C. for 4 h. to provide the desired NiO-Sm₂ O₃ catalyst. The surface area of the catalyst was 2.35 m². g⁻¹.

EXAMPLE-22

Preparation of NiO-Nd₂ O₃ catalyst with Ni/Nd mole ratio of 1.0.

Finely ground 10.0 g of Nd(NO₃)₃.sup.. 6H₂ O, finely ground 6.63 g of Ni(NO₃)₂.sup.. 6H₂ O, and 2 ml of deionized water are thoroughly mixed and the resulting mixture is dried in air oven at 120° C. for 8 h. The dried mass is then decomposed at 610° C. in air for 6 h. The decomposed mass is then powdered, pressed binder-free at 4 ton pressure and crushed to 22-30 mesh size particles. The catalyst particles are then calcined in presence of air at 910° C. for 5 h to provide the desired NiO-Nd₂ O₃ catalyst. The surface area of the catalyst was 2.60 m². g⁻¹.

EXAMPLE-23

Preparation of NiO-La₂ O₃ catalyst with Ni/La mole ratio of 0.5.

Finely ground 10.0 g La₂ (CO₃)₃.sup.. xH₂ O, finely ground 6.35 g Ni(NO₃)₂.sup.. 6H₂ O, and 17 ml deionized water are thoroughly mixed and the resulting paste is dried in air oven at 130° C. for 6 h. The dried mass is then decomposed at 710° C. in air for 4 h. The decomposed mass is then powdered, pressed binder-free at 5 ton pressure and crushed to 22-30 mesh size particles. The catalyst particles are then calcined in air at 930° C. for 5 h to provide the desired NiO-La₂ O₃ catalyst. The surface area of the catalyst was 3.80 m². g⁻¹.

EXAMPLE-24

Preparation of CoO-Yb₂ O₃ catalyst with Co/Yb mole ratio of 1.0.

Finely ground 7.0 g of Yb₂ O₃, finely ground 10.34 g of Co(NO₃)₂.sup.. 6H₂ O and 1 ml of deionized water are thoroughly mixed and the resulting mixture is dried in air at 120° C. for 4 h. The dried mass is decomposed in air at 620° C. for 6 h. The decomposed mass is then powdered, pressed binder-free at 4 ton pressure and crushed to 22-30 mesh size particles. The catalyst particles are then calcined in air at 900° C. for 6 h to provide the desired CoO-Yb₂ O₃ catalyst. The surface area of the catalyst was 4.59 m². g⁻¹.

EXAMPLE-25

Preparation of CoO-Eu₂ O₃ catalyst with Co/Eu mole ratio of 1.0.

Finely ground 12.0 g of Eu₂ O₃, finely ground 19.87 g of Co(NO₃)₂.sup.. 6H₂ O and 4 ml of deionized water are thoroughly mixed and the resulting mixture is then dried in air at 130° C. for 5 h. The dried mass is decomposed in air at 600° C. for 4 h. The decomposed mass is then powdered, pressed binder-free at 4 ton pressure and crushed to 22-30 mesh size particles. The catalyst particles are then calcined in air at 910° C. for 4 h to provide the desired CoO-Eu₂ O₃ catalyst. The surface area of the catalyst was 1.87 m². g⁻¹.

EXAMPLE-26

Use of the catalysts, the preparation of which is described in Examples 18-25, for the oxidative conversion of methane to synthesis gas. The reaction over the catalysts was carried out in the reactor and by the procedure similar to that described in Example-13, at the following reaction conditions.

Feed composition:67 mol % CH₄ and 33 mol % O₂

Gas hourly space velocity:515,000 cm³. g⁻¹. h⁻¹ (GHSV)

Pressure:1.3±0.2 atm.

The results obtained using the catalysts at different reaction temperatures are presented in Table-2.

                                      TABLE 2                                      __________________________________________________________________________     Performance of the catalysts, preparation of which is described in             EXAMPLES 18-25, in oxidative conversion of methane to synthesis gas            (i.e. CO and H.sub.2).                                                                 Example in                                                                     which cata-                                                                          Reaction                                                                             CH.sub.4 -                                                                          Selec-                                                                              Selec-                                                   lyst prepa-                                                                          tempera-                                                                             conver-                                                                             tivity                                                                              tivity                                                                             H.sub.2 /CO                                          ration is                                                                            ture  sion for CO                                                                              for H.sub.2                                                                        mole                                         Catalyst                                                                               described                                                                            (°C.)                                                                         (%)  (%)  (%) ratio                                        __________________________________________________________________________     NiO--Eu.sub.2 O.sub.3                                                                  Example-18                                                                           702   84.8 93.0 89.1                                                                               1.92                                         (Ni/Eu = 1.0) 600   81.8 91.4 87.5                                                                               1.91                                                       322   75.4 85.7 81.1                                                                               1.89                                         NiO--Eu.sub.2 O.sub.3                                                                  Example-19                                                                           703   66.1 89.1 78.8                                                                               1.77                                         (Ni/Eu = 0.1) 503   57.7 84.2 70.3                                                                               1.67                                         NiO--Yb.sub.2 O.sub.3                                                                  Example-20                                                                           704   86.6 95.5 96.1                                                                               2.01                                         (Ni/Yb = 4.0) 602   78.7 91.0 93.6                                                                               2.06                                                       300   70.9 83.6 87.0                                                                               2.08                                         NiO--Sm.sub.2 O.sub.3                                                                  Example-21                                                                           702   81.0 94.9 92.8                                                                               1.96                                         (Ni/Sm = 1.0) 602   70.6 91.7 90.3                                                                               1.97                                                       326   63.3 84.9 84.1                                                                               1.98                                         NiO-- Nd.sub.2 O.sub.3                                                                 Example-22                                                                           702   77.3 94.7 93.6                                                                               1.98                                         (Ni/Nd = 1.0) 603   73.3 89.5 90.2                                                                               2.02                                                       502   68.9 87.5 87.3                                                                               2.00                                         NiO--La.sub.2 O.sub.3                                                                  Example-23                                                                           702   69.4 90.6 86.7                                                                               1.91                                         (Ni/La = 1.0) 601   66.2 87.3 83.3                                                                               1.91                                         CoO--Yb.sub.2 O.sub.3                                                                  Example-24                                                                           702   79.2 89.9 88.4                                                                               1.97                                         (Co/Yb = 1.0) 596   72.6 87.2 86.1                                                                               1.97                                         CoO--Eu.sub.2 O.sub.3                                                                  Example-25                                                                           704   62.0 88.1 84.9                                                                               1.91                                         (Co/Eu = 1.0)                                                                  __________________________________________________________________________

EXAMPLE-27

Preparation of NiO-MgO-La₂ O₃ catalyst (Ni:Mg:La=1:1:0.1).

Finely ground 6.25 g of MgCO₃, 2.90 g of La(NO₃)₃.sup.. 6H₂ O, 19.46 g of Ni(NO₃)₂.sup.. 6H₂ O and 8 ml deionized water are thoroughly mixed and the resulting mixture is dried in air at 120° C. for 6 h. The dried mass is decomposed in air at 600° C. for 6 h. The decomposed mass is then powdered, pressed binder-free at 5 ton pressure and crushed to 22-30 mesh size particles. The catalyst particles are then calcined in air at 900° C. for 6 h to provide the desired NiO-MgO-La₂ O₃ catalyst. The surface area of the catalyst was 4.63 m². g⁻¹.

EXAMPLE-28

Preparation of NiO-CaO-Sm₂ O₃ catalyst (Ni:Ca:Sm=1:1:0.1).

Finely ground 4.96 g of Ca(OH)₂, 2.55 g of (CH₃ CO₂)₃ Sm.sup.. 3H₂ O, 19.46 g of Ni(NO₃)₂.sup.. 6H₂ O and 5 ml of deionized water are thoroughly mixed and the resulting mixture is dried in air at 130° C. for 4 h. The dried mass is decomposed in air at 610° C. for 6 h. The decomposed mass is then powdered, pressed binder-free at 4 ton pressure and crushed to 22-30 mesh size particles. The catalyst particles are then calcined in air 930° C. for 5 h to provide the desired NiO-CaO-Sm₂ O₃ catalyst. The surface area of the catalyst was 6.05 m². g⁻¹.

EXAMPLE-29

Use of the catalysts, the preparation of which is described in EXAMPLES 27, 28 and 3, for the oxidative conversion of methane to synthesis gas. The reaction over the catalysts was carried out in the reactor and by the procedure similar to that described in Example-2, at the following reaction conditions.

    ______________________________________                                         Feed composition:                                                                              67 mol % CH.sub.4 and 37 mol % O.sub.2                         Gas hourly space velocity:                                                                     516,000 cm.sup.3 · g.sup.-1 · h.sup.-1       (GHSV)                                                                         Pressure:       1.3 ± 0.1 atm.                                              ______________________________________                                    

The results obtained using the catalysts at different reaction temperatures are presented in Table-3.

                                      TABLE 3                                      __________________________________________________________________________     Performance of the catalysts, preparation of which is described in             EXAMPLES 27, 28 and 3, in oxidative conversion of methane to                   synthesis gas (i.e. CO and H.sub.2).                                                     Example in                                                                     which cata-                                                                          Reaction                                                                            CH.sub.4 -                                                                           Selec-                                                                             Selec-                                                    lyst prepa-                                                                          tempera-                                                                            conver-                                                                              tivity                                                                             tivity                                                                             H.sub.2 /CO                                           ration is                                                                            ture sion  for CO                                                                             for H.sub.2                                                                        mole                                        Catalyst  described                                                                            (°C.)                                                                        (%)   (%) (%) ratio                                       __________________________________________________________________________     NiO--MgO--La.sub.2 O.sub.3                                                               Example-27                                                                           703  73.0  94.5                                                                               93.9                                                                               1.99                                        (Ni:Mg:La =     600  65.3  88.5                                                                               90.2                                                                               2.04                                        1:1:0.1)                                                                                       496  58.6  82.9                                                                               85.9                                                                               2.07                                        NiO--CaO--Sm.sub.2 O.sub.3                                                               Example-28                                                                           500  74.2  86.0                                                                               89.3                                                                               2.08                                        (Ni:Ca:Sm =                                                                    1:1:0.1)                                                                       NiO--MgO.sub.--Sm.sub.2 O.sub.3                                                          Example-3                                                                            702  81.7  95.0                                                                               96.6                                                                               2.03                                        (Ni:Mg:Sm =     602  76.8  92.0                                                                               93.1                                                                               2.02                                        1:1:0.1)                                                                                       507  69.1  86.7                                                                               89.7                                                                               2.07                                                        326  61.9  79.2                                                                               87.0                                                                               2.20                                        __________________________________________________________________________

EXAMPLE-30

Preparation of NiO-Al₂ O₃ -La₂ O₃ catalyst (Ni:Al:La=1:1:1).

Finely ground 4.10 g of Al₂ O₃, 17.39 g of La(NO₃)₃.sup.. 6H₂ O, 11.68 g of Ni(NO₃)₂.sup.. 6H₂ O and 4 ml of deionized water are thoroughly mixed and the resulting mixture is dried in air at 120° C. for 6 h. The dried mass is decomposed at 610° C. for 5 h. The decomposed mass is then powdered, pressed binder-free at 5 ton pressure and crushed to 22-30 mesh size particles. The catalyst particles are then calcined in air at 910° C. for 5 h to provide the NiO-Al₂ O₃ -La₂ O₃ catalyst. The surface area of the catalyst was 12.08 m². g⁻¹.

EXAMPLE-31

Use of the catalysts, the preparation of which is described in EXAMPLES 30 & 4, for the oxidative conversion of methane to synthesis gas. The reaction over the catalysts was carried out in the reactor and by the procedure similar to that described in Example-2, at the following reaction conditions.

    ______________________________________                                         Feed composition:                                                                              67 mol % CH.sub.4 and 33 mol % O.sub.2                         Gas hourly space velocity:                                                                     515,000 cm.sup.3 · g.sup.-1 · h.sup.-1       (GHSV)                                                                         Pressure:       1.35 atm.                                                      ______________________________________                                    

The results obtained using the catalysts at different reaction temperatures are presented in Table -4.

                                      TABLE 4                                      __________________________________________________________________________     Performance of the catalysts, preparation of which is described in             EXAMPLES 30 & 4, in oxidative conversion of methane to synthesis               gas (i.e. CO and H.sub.2).                                                                Example in                                                                     which cata-                                                                          Reaction                                                                            CH.sub.4 -                                                                          Selec-                                                                             Selec-                                                     lyst prepa-                                                                          tempera-                                                                            conver-                                                                             tivity                                                                             tivity                                                                             H.sub.2 /CO                                            ration is                                                                            ture sion for CO                                                                             for H.sub.2                                                                        mole                                        Catalyst   described                                                                            (°C.)                                                                        (%)  (%) (%) ratio                                       __________________________________________________________________________     NiO--Al.sub.2 O.sub.3 --La.sub.2 O.sub.3                                                  Example-30                                                                           701  84.3 94.6                                                                               94.5                                                                               2.00                                        (Ni:Al:La =      604  77.7 89.6                                                                               92.6                                                                               2.07                                        1:1:1)                                                                                          496  72.3 87.1                                                                               90.3                                                                               2.07                                        NiO--Al.sub.2 O.sub.3 --Yb.sub.2 O.sub.3                                                  Example-4                                                                            702  89.5 95.9                                                                               94.9                                                                               1.98                                        (Ni:Al:Yb =      601  82.0 92.6                                                                               92.6                                                                               2.00                                        1:1:1)                                                                                          500  79.4 90.7                                                                               90.8                                                                               2.00                                                         297  69.7 84.8                                                                               86.1                                                                               2.03                                        __________________________________________________________________________ 

We claim:
 1. A process for the production of a gas comprising a H₂ and CO by oxidative conversion of a gas comprising methane, said process consists essentially ofa) O₂ and a hydrocarbon feed mixture comprising methane over a composite catalyst represented by a formula T_(m).sup.. N_(m).sup.. R.sup.. O_(p) wherein T is a transition element selected from Ni, Co, Ru, Rh, or a mixture of two or more thereof; m is T/R mole ratio, wherein m is from 0.01 to about 100; N is selected from Mg, Ca, or a mixture thereof; n is N/R mole ratio, wherein n is from greater than 0 to 100; R is a rare earth element selected from La, Ce, Pr, Nd, Pm, Sm, Eu, Gd, Tb, Dy, Ho, Er, Tm, Tb and Lu or a mixture of two or more thereof, O is oxygen and p is number of oxygen atoms required to fulfill the valence requirement of the elements in the catalyst, in a fixed bed reactor at a pressure of from 0.5-50 atm, a temperature of from 200°-1000° C., a gas hourly space velocity in the range of 10³ -10⁸ cm³ g⁻¹.spsb..^(h-1), and a hydrocarbon/O₂ mole ratio in the feed mixture in the range of 1.6-10 and b) separating water vapors, unconverted reactants and feed components other than the reactants and carbon dioxide from the product stream.
 2. A process according to claim 1, wherein the pressure is from about 1 to 5 atm.
 3. A process according to claim 1, wherein the reaction temperature ranges from about 250° to 900° C.
 4. A process according to claim 1, wherein the gas hourly space velocity ranges from 1×10⁴ to 5×10⁶ cm³. g⁻ 1.sup.. h⁻
 1. 5. A process according to claim 1, wherein the natural gas/O₂ mole ratio ranges from 1.8 to 4.0.
 6. A process according claim 1, wherein the concentration of methane in the feed ranges from 20 to 80 mole %.
 7. A process according to claim 1, wherein the concentration of oxygen in feed ranges from 10 to 36 mole %.
 8. A process according to claim 1, wherein the H₂ O/natural gas mole ratio in the feed ranges from 0 to
 2. 9. A process according to claim 1, where the gas comprising H₂ and CO is synthesis gas.
 10. A process according to claim 1, wherein the gaseous reactant feed mixture comprises natural gas and air. 